VALOX? Resin VX4920 - Europe
聚丁烯對苯二甲酸酯
SABIC
Product Description:
VALOX VX4920 is a 20% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry.
點擊下載VALOXVX4920物性表：
聚丁烯對苯二甲酸酯
SABIC
Product Description:
VALOX VX4920 is a 20% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry.
|
用途
|
|
| 物理性能 |
額定值
|
單位制
|
測試方法
|
|
密度 / 比重
|
1.38
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔體流動速率）
|
ASTM D1238 | ||
|
200°C/3.8 kg
|
17
|
g/10 min
|
|
|
265°C/5.0 kg
|
35
|
g/10 min
|
|
|
熔融體積流量（MVR）
|
ISO 1133 | ||
|
250°C/5.0 kg
|
17
|
cm3/10min
|
|
|
265°C/5.0 kg
|
30
|
cm3/10min
|
|
|
收縮率
|
內(nèi)部方法 | ||
|
垂直 2
|
0.40 到 0.80
|
%
|
|
|
流動 2
|
0.20 到 0.40
|
%
|
|
|
流動 : 3.20 mm
|
0.30 到 0.60
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
飽和, 23°C
|
0.76
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.27
|
%
|
|
| 硬度 |
額定值
|
單位制
|
測試方法
|
|
洛氏硬度 (R 計秤)
|
118
|
|
ISO 2039-2 |
|
球壓硬度 (H 358/30)
|
130
|
MPa
|
ISO 2039-1 |
| 機械性能 |
額定值
|
單位制
|
測試方法
|
|
拉伸模量
|
|||
|
-- 3
|
7200
|
MPa
|
ASTM D638 |
|
--
|
7200
|
MPa
|
ISO 527-2/1 |
|
抗張強度
|
|||
|
屈服 4
|
105
|
MPa
|
ASTM D638 |
|
屈服
|
105
|
MPa
|
ISO 527-2/5 |
|
斷裂 4
|
105
|
MPa
|
ASTM D638 |
|
斷裂
|
105
|
MPa
|
ISO 527-2/5 |
|
伸長率
|
|||
|
屈服 4
|
3.0
|
%
|
ASTM D638 |
|
屈服
|
3.0
|
%
|
ISO 527-2/5 |
|
斷裂 4
|
3.0
|
%
|
ASTM D638 |
|
斷裂
|
3.0
|
%
|
ISO 527-2/5 |
|
彎曲模量
|
|||
|
50.0 mm 跨距 5
|
5500
|
MPa
|
ASTM D790 |
|
-- 6
|
5700
|
MPa
|
ISO 178 |
|
彎曲應(yīng)力
|
|||
|
-- 6, 7
|
155
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
160
|
MPa
|
ASTM D790 |
|
斷裂, 50.0 mm 跨距 5
|
160
|
MPa
|
ASTM D790 |
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪)
|
80.0
|
mg
|
內(nèi)部方法 |
|
彎曲應(yīng)變 - at Break 8
|
4.0
|
%
|
ISO 178 |
| 沖擊性能 |
額定值
|
單位制
|
測試方法
|
|
簡支梁缺口沖擊強度
|
|||
|
-30°C 9
|
5.0
|
kJ/m2
|
ISO 179/1eA |
|
-30°C
|
8.0
|
kJ/m2
|
ISO 179/2C |
|
23°C 9
|
6.0
|
kJ/m2
|
ISO 179/1eA |
|
23°C
|
10
|
kJ/m2
|
ISO 179/2C |
|
簡支梁無缺口沖擊強度
|
|||
|
-30°C 9
|
40
|
kJ/m2
|
ISO 179/1eU, ISO 179/2U |
|
23°C 9
|
45
|
kJ/m2
|
ISO 179/1eU |
|
23°C
|
55
|
kJ/m2
|
ISO 179/2U |
|
懸壁梁缺口沖擊強度
|
|||
|
-30°C
|
70
|
J/m
|
ASTM D256 |
|
0°C
|
75
|
J/m
|
ASTM D256 |
|
23°C
|
80
|
J/m
|
ASTM D256 |
|
-30°C 10
|
7.0
|
kJ/m2
|
ISO 180/1A |
|
0°C 10
|
7.0
|
kJ/m2
|
ISO 180/1A |
|
23°C 10
|
7.0
|
kJ/m2
|
ISO 180/1A |
|
無缺口懸臂梁沖擊
|
|||
|
-30°C
|
610
|
J/m
|
ASTM D4812 |
|
23°C
|
680
|
J/m
|
ASTM D4812 |
|
-30°C 10
|
40
|
kJ/m2
|
ISO 180/1U |
|
23°C 10
|
45
|
kJ/m2
|
ISO 180/1U |
|
裝有測量儀表的落鏢沖擊 (23°C, Total Energy)
|
50.0
|
J
|
ASTM D3763 |
| 熱性能 |
額定值
|
單位制
|
測試方法
|
|
載荷下熱變形溫度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
210
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11
|
209
|
°C
|
ISO 75-2/Be |
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
|
210
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
170
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11
|
179
|
°C
|
ISO 75-2/Ae |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
|
170
|
°C
|
ISO 75-2/Af |
|
維卡軟化溫度
|
|||
|
--
|
220
|
°C
|
ASTM D1525 12, ISO 306/A50 12 |
|
--
|
170
|
°C
|
ASTM D1525 13, ISO 306/B50 13 |
|
--
|
165
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (123 到 127°C)
|
通過
|
|
IEC 60695-10-2 |
|
線形熱膨脹系數(shù)
|
|||
|
流動 : -40 到 40°C
|
3.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
流動 : -40 到 40°C
|
2.9E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
流動 : 23 到 60°C
|
3.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
流動 : 23 到 150°C
|
2.4E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 40°C
|
1.1E-4
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -40°C
|
7.7E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : 23 到 60°C
|
1.1E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : 23 到 150°C
|
1.6E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
導熱系數(shù)
|
0.25
|
W/m/K
|
ISO 8302 |
| 電氣性能 |
額定值
|
單位制
|
測試方法
|
|
表面電阻率
|
> 1.0E+15
|
ohms
|
IEC 60093 |
|
體積電阻率
|
> 1.0E+15
|
ohms·cm
|
ASTM D257, IEC 60093 |
|
介電強度
|
|||
|
1.60 mm, in Oil
|
28
|
kV/mm
|
ASTM D149 |
|
3.20 mm, in Oil
|
24
|
kV/mm
|
ASTM D149 |
|
1.60 mm, 在油中
|
28
|
kV/mm
|
IEC 60243-1 |
|
3.20 mm, 在油中
|
24
|
kV/mm
|
IEC 60243-1 |
|
介電常數(shù)
|
|||
|
1 MHz
|
3.40
|
|
ASTM D150, IEC 60250 |
|
50 Hz
|
3.40
|
|
IEC 60250 |
|
60 Hz
|
3.40
|
|
IEC 60250 |
|
耗散因數(shù)
|
|||
|
1 MHz
|
0.020
|
|
ASTM D150, IEC 60250 |
|
50 Hz
|
2.4E-3
|
|
IEC 60250 |
|
60 Hz
|
2.4E-3
|
|
IEC 60250 |
|
相比耐漏電起痕指數(shù)(CTI)
|
PLC 1
|
|
UL 746 |
| 可燃性 |
額定值
|
單位制
|
測試方法
|
|
UL 阻燃等級 (1.6 mm, Testing by SABIC)
|
HB
|
|
UL 94 |
|
灼熱絲易燃指數(shù) (1.0 mm)
|
750
|
°C
|
IEC 60695-2-12 |
| 充模分析 |
額定值
|
單位制
|
測試方法
|
|
熔體粘度 (260°C, 1500 sec^-1)
|
175
|
Pa·s
|
ISO 11443 |
| 補充信息 |
額定值
|
單位制
|
測試方法
|
|
填充物
|
20
|
%
|
ASTM D229 |
| 注射 |
額定值
|
單位制
|
|
|
干燥溫度
|
110 到 120
|
°C
|
|
|
干燥時間
|
2.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
料斗溫度
|
40 到 60
|
°C
|
|
|
料筒后部溫度
|
230 到 245
|
°C
|
|
|
料筒中部溫度
|
240 到 255
|
°C
|
|
|
料筒前部溫度
|
245 到 265
|
°C
|
|
|
射嘴溫度
|
240 到 260
|
°C
|
|
|
加工（熔體）溫度
|
250 到 270
|
°C
|
|
|
模具溫度
|
40 到 100
|
°C
|
| 備注 |
| 1UL 黃卡含有 UL 驗證的易燃性和電氣特性。UL Prospector 持續(xù)努力在 Prospector 中將黃卡鏈接至單個塑料材料，然而此列表可能未包括所有相應(yīng)鏈接。重要的是，我們對 Prospector 中找到的這些黃卡和塑料材料之間的關(guān)聯(lián)進行驗證。如需完整的黃卡列 表，請訪問 UL 黃卡搜索。 |
| 2Tensile Bar |
| 35.0 mm/min |
| 4類型 1, 5.0 mm/min |
| 51.3 mm/min |
| 62.0 mm/min |
| 7at Yield |
| 82 mm/min |
| 980*10*4 sp=62mm |
| 1080*10*4 mm |
| 11120*10*4 mm |
| 12速率 A (50°C/h), 壓 力1 (10N) |
| 13速率 A (50°C/h), 載荷2 (50N) |
點擊下載VALOXVX4920物性表：