XENOY? Resin HX6600HP - Asia
聚碳酸酯+PBT
SABIC
Product Description:
Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
點(diǎn)擊下載XENOYHX6600HP物性表：
聚碳酸酯+PBT
SABIC
Product Description:
Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
|
用途
|
|
| 物理性能 |
額定值
|
單位制
|
測試方法
|
|
密度 / 比重
|
1.21
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔體流動速率） (250°C/5.0 kg)
|
11
|
g/10 min
|
ASTM D1238 |
|
熔融體積流量（MVR） (250°C/5.0 kg)
|
10
|
cm3/10min
|
ISO 1133 |
|
收縮率 - 流動 (3.20 mm)
|
1.2 到 1.6
|
%
|
內(nèi)部方法 |
|
吸水率
|
ISO 62 | ||
|
飽和, 23°C
|
0.40
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.050
|
%
|
| 機(jī)械性能 |
額定值
|
單位制
|
測試方法
|
|
拉伸模量
|
|||
|
-- 1
|
1900
|
MPa
|
ASTM D638 |
|
--
|
1900
|
MPa
|
ISO 527-2/1 |
|
抗張強(qiáng)度
|
|||
|
屈服 2
|
43.0
|
MPa
|
ASTM D638 |
|
屈服
|
44.0
|
MPa
|
ISO 527-2/50 |
|
斷裂 2
|
35.0
|
MPa
|
ASTM D638 |
|
斷裂
|
37.0
|
MPa
|
ISO 527-2/50 |
|
伸長率
|
|||
|
屈服 2
|
4.0
|
%
|
ASTM D638 |
|
屈服
|
4.0
|
%
|
ISO 527-2/50 |
|
斷裂 2
|
150
|
%
|
ASTM D638 |
|
斷裂
|
100
|
%
|
ISO 527-2/50 |
|
彎曲模量
|
|||
|
50.0 mm 跨距 3
|
1900
|
MPa
|
ASTM D790 |
|
-- 4
|
1800
|
MPa
|
ISO 178 |
|
彎曲應(yīng)力
|
|||
|
-- 4, 5
|
64.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 3
|
43.0
|
MPa
|
ASTM D790 |
| 沖擊性能 |
額定值
|
單位制
|
測試方法
|
|
簡支梁缺口沖擊強(qiáng)度 6 (23°C)
|
70
|
kJ/m2
|
ISO 179/1eA |
|
簡支梁無缺口沖擊強(qiáng)度 6 (-30°C)
|
無斷裂
|
|
ISO 179/1eU |
|
懸壁梁缺口沖擊強(qiáng)度
|
|||
|
-30°C
|
750
|
J/m
|
ASTM D256 |
|
23°C
|
800
|
J/m
|
ASTM D256 |
|
-30°C 7
|
20
|
kJ/m2
|
ISO 180/1A |
|
23°C 7
|
65
|
kJ/m2
|
ISO 180/1A |
|
無缺口伊佐德沖擊強(qiáng)度 7 (-40°C)
|
無斷裂
|
|
ISO 180/1U |
|
裝有測量儀表的落鏢沖擊
|
|||
|
23°C, Total Energy
|
100
|
J
|
ASTM D3763 |
|
--
|
100
|
J
|
ISO 6603-2 |
| 熱性能 |
額定值
|
單位制
|
測試方法
|
|
熱變形溫度
|
|||
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7
|
95.0
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
60.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7
|
60.0
|
°C
|
ISO 75-2/Af |
|
維卡軟化溫度
|
|||
|
--
|
117
|
°C
|
ASTM D1525 8, ISO 306/B50 8 |
|
--
|
120
|
°C
|
ISO 306/B120 |
|
線形熱膨脹系數(shù)
|
|||
|
流動 : -40 到 40°C
|
1.0E-4
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
流動 : 23 到 60°C
|
1.3E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 40°C
|
1.0E-4
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -40°C
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
| 充模分析 |
額定值
|
單位制
|
測試方法
|
|
熔體粘度 (260°C, 1500 sec^-1)
|
210
|
Pa·s
|
ISO 11443 |
| 注射 |
額定值
|
單位制
|
|
|
干燥溫度
|
90 到 100
|
°C
|
|
|
干燥時(shí)間
|
2.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
料斗溫度
|
40 到 60
|
°C
|
|
|
料筒后部溫度
|
230 到 250
|
°C
|
|
|
料筒中部溫度
|
240 到 265
|
°C
|
|
|
料筒前部溫度
|
250 到 270
|
°C
|
|
|
射嘴溫度
|
250 到 265
|
°C
|
|
|
加工（熔體）溫度
|
255 到 270
|
°C
|
|
|
模具溫度
|
60 到 80
|
°C
|
| 備注 |
| 15.0 mm/min |
| 2類型 1, 50 mm/min |
| 31.3 mm/min |
| 42.0 mm/min |
| 5at Yield |
| 680*10*4 sp=62mm |
| 780*10*4 mm |
| 8速率 A (50°C/h), 載荷2 (50N) |
點(diǎn)擊下載XENOYHX6600HP物性表：
備注：以上數(shù)據(jù)表中的信息由 HuasuStar - 華塑之星 從該材料的生產(chǎn)商處獲得。HuasuStar - 華塑之星 盡最大努力確保此數(shù)據(jù)的準(zhǔn)確性。 但是 HuasuStar - 華塑之星 對這些數(shù)據(jù)值不承擔(dān)任何責(zé)任，并強(qiáng)烈建議在最終選擇材料前，就數(shù)據(jù)值與材料生產(chǎn)商進(jìn)行驗(yàn)證。
如需購買此材料，請聯(lián)系我們：0769-87796856 huasu@huasustar.com