聚碳酸酯+丙烯腈丁二烯苯乙烯
SABIC
Product Description:
CYCOLOY HCX1640 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is a biocompatible (ISO10993 or USP Class VI) grade for medical devices and pharmaceutical applications. It has improved heat, flow and impact balance as compared with conventional PC/ABS blends. This grade adheres to our healthcare management of change policy.
點(diǎn)擊下載CYCOLOY HCX1640物性表：
聚碳酸酯+丙烯腈丁二烯苯乙烯
SABIC
Product Description:
CYCOLOY HCX1640 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is a biocompatible (ISO10993 or USP Class VI) grade for medical devices and pharmaceutical applications. It has improved heat, flow and impact balance as compared with conventional PC/ABS blends. This grade adheres to our healthcare management of change policy.
|
用途
|
|
| 物理性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
密度 / 比重
|
1.15
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率（熔體流動(dòng)速率） (260°C/5.0 kg)
|
19
|
g/10 min
|
ASTM D1238 |
|
熔融體積流量（MVR） (260°C/5.0 kg)
|
18
|
cm3/10min
|
ISO 1133 |
|
收縮率 - 流動(dòng) (3.20 mm)
|
0.40 到 0.60
|
%
|
內(nèi)部方法 |
|
吸水率
|
ISO 62 | ||
|
飽和, 23°C
|
0.40
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.10
|
%
|
| 機(jī)械性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
拉伸模量
|
|||
|
-- 1
|
2400
|
MPa
|
ASTM D638 |
|
--
|
2400
|
MPa
|
ISO 527-2/1 |
|
抗張強(qiáng)度
|
|||
|
屈服 2
|
55.0
|
MPa
|
ASTM D638 |
|
屈服
|
55.0
|
MPa
|
ISO 527-2/50 |
|
斷裂 2
|
50.0
|
MPa
|
ASTM D638 |
|
斷裂
|
50.0
|
MPa
|
ISO 527-2/50 |
|
伸長(zhǎng)率
|
|||
|
屈服 2
|
5.0
|
%
|
ASTM D638 |
|
屈服
|
5.0
|
%
|
ISO 527-2/50 |
|
斷裂 2
|
> 50
|
%
|
ASTM D638 |
|
斷裂
|
> 50
|
%
|
ISO 527-2/50 |
|
彎曲模量
|
|||
|
50.0 mm 跨距 3
|
2300
|
MPa
|
ASTM D790 |
|
-- 4
|
2300
|
MPa
|
ISO 178 |
|
彎曲應(yīng)力
|
|||
|
-- 4, 5
|
85.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 3
|
85.0
|
MPa
|
ASTM D790 |
| 沖擊性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 6
|
ISO 179/1eA | ||
|
-30°C
|
20
|
kJ/m2
|
|
|
23°C
|
40
|
kJ/m2
|
|
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 6
|
ISO 179/1eU | ||
|
-30°C
|
無(wú)斷裂
|
|
|
|
23°C
|
無(wú)斷裂
|
|
|
|
懸壁梁缺口沖擊強(qiáng)度
|
|||
|
-30°C
|
300
|
J/m
|
ASTM D256 |
|
23°C
|
550
|
J/m
|
ASTM D256 |
|
23°C 7
|
150
|
J/m
|
內(nèi)部方法 |
|
-30°C 8
|
20
|
kJ/m2
|
ISO 180/1A |
|
23°C 8
|
40
|
kJ/m2
|
ISO 180/1A |
|
無(wú)缺口伊佐德沖擊強(qiáng)度 8
|
ISO 180/1U | ||
|
-30°C
|
無(wú)斷裂
|
|
|
|
23°C
|
無(wú)斷裂
|
|
|
|
裝有測(cè)量?jī)x表的落鏢沖擊 (23°C, Total Energy)
|
65.0
|
J
|
ASTM D3763 |
| 熱性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
載荷下熱變形溫度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
122
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 3.20 mm
|
108
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
|
108
|
°C
|
ISO 75-2/Af |
|
維卡軟化溫度
|
|||
|
--
|
130
|
°C
|
ASTM D1525 9, ISO 306/B50 9 |
|
--
|
132
|
°C
|
ISO 306/B120 |
|
線(xiàn)形熱膨脹系數(shù)
|
|||
|
流動(dòng) : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
垂直 : -40 到 40°C
|
7.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -40°C
|
7.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
| 注射 |
額定值
|
單位制
|
|
|
干燥溫度
|
100 到 110
|
°C
|
|
|
干燥時(shí)間
|
2.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
料斗溫度
|
60 到 80
|
°C
|
|
|
料筒后部溫度
|
230 到 260
|
°C
|
|
|
料筒中部溫度
|
250 到 290
|
°C
|
|
|
料筒前部溫度
|
250 到 290
|
°C
|
|
|
射嘴溫度
|
240 到 280
|
°C
|
|
|
加工（熔體）溫度
|
260 到 290
|
°C
|
|
|
模具溫度
|
60 到 90
|
°C
|
| 備注 |
| 15.0 mm/min |
| 2類(lèi)型 1, 50 mm/min |
| 31.3 mm/min |
| 42.0 mm/min |
| 5at Yield |
| 680*10*4 sp=62mm |
| 7Double-gated |
| 880*10*4 mm |
| 9速率 A (50°C/h), 載荷2 (50N) |
點(diǎn)擊下載CYCOLOY HCX1640物性表：
備注：以上數(shù)據(jù)表中的信息由 HuasuStar - 華塑之星 從該材料的生產(chǎn)商處獲得。HuasuStar - 華塑之星 盡最大努力確保此數(shù)據(jù)的準(zhǔn)確性。 但是 HuasuStar - 華塑之星 對(duì)這些數(shù)據(jù)值不承擔(dān)任何責(zé)任，并強(qiáng)烈建議在最終選擇材料前，就數(shù)據(jù)值與材料生產(chǎn)商進(jìn)行驗(yàn)證。
如需購(gòu)買(mǎi)此材料，請(qǐng)聯(lián)系我們：0769-87796856 huasu@huasustar.com
塑料行業(yè)新聞動(dòng)態(tài)?
-
2024-01-08