VALOX? Resin VX4910 - Europe
聚對苯二甲酸丁二酯 + ASA
SABIC
Product Description:
10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.
點擊下載VALOXVX4910物性表：
聚對苯二甲酸丁二酯 + ASA
SABIC
Product Description:
10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.
|
Uses
|
|
| Physical |
額定值
|
單位制
|
測試方法
|
|
Density / Specific Gravity
|
1.30
|
g/cm3
|
ASTM D792, ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ASTM D1238 | ||
|
200°C/3.8 kg
|
20
|
g/10 min
|
|
|
265°C/5.0 kg
|
40
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
ISO 1133 | ||
|
250°C/5.0 kg
|
25
|
cm3/10min
|
|
|
265°C/5.0 kg
|
35
|
cm3/10min
|
|
|
Molding Shrinkage - 流動 (3.20 mm)
|
0.60 到 0.80
|
%
|
Internal Method |
| Hardness |
額定值
|
單位制
|
測試方法
|
|
Rockwell Hardness (R 計秤)
|
120
|
|
ISO 2039-2 |
|
Ball Indentation Hardness (H 358/30)
|
100
|
MPa
|
ISO 2039-1 |
| Mechanical |
額定值
|
單位制
|
測試方法
|
|
Tensile Modulus
|
|||
|
-- 1
|
4600
|
MPa
|
ASTM D638 |
|
--
|
4600
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
屈服 2
|
80.0
|
MPa
|
ASTM D638 |
|
屈服
|
80.0
|
MPa
|
ISO 527-2/5 |
|
斷裂 2
|
80.0
|
MPa
|
ASTM D638 |
|
斷裂
|
80.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Elongation
|
|||
|
屈服 2
|
3.0
|
%
|
ASTM D638 |
|
屈服
|
3.0
|
%
|
ISO 527-2/5 |
|
斷裂 2
|
3.0
|
%
|
ASTM D638 |
|
斷裂
|
3.0
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|||
|
50.0 mm Span 3
|
3400
|
MPa
|
ASTM D790 |
|
-- 4
|
3800
|
MPa
|
ISO 178 |
|
Flexural Stress
|
|||
|
-- 4, 5
|
120
|
MPa
|
ISO 178 |
|
-- 4, 6
|
115
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm Span 3
|
115
|
MPa
|
ASTM D790 |
|
斷裂, 50.0 mm Span 3
|
115
|
MPa
|
ASTM D790 |
|
彎曲應(yīng)變 - at Break 7
|
4.0
|
%
|
ISO 178 |
| Impact |
額定值
|
單位制
|
測試方法
|
|
Charpy Notched Impact Strength
|
ISO 179/2C | ||
|
-30°C
|
5.0
|
kJ/m2
|
|
|
23°C
|
6.0
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/2U | ||
|
-30°C
|
20
|
kJ/m2
|
|
|
23°C
|
45
|
kJ/m2
|
|
|
Notched Izod Impact
|
|||
|
-30°C
|
45
|
J/m
|
ASTM D256 |
|
0°C
|
50
|
J/m
|
ASTM D256 |
|
23°C
|
55
|
J/m
|
ASTM D256 |
|
-30°C 8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
0°C 8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
23°C 8
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|||
|
-30°C
|
340
|
J/m
|
ASTM D4812 |
|
23°C
|
440
|
J/m
|
ASTM D4812 |
|
-30°C 8
|
25
|
kJ/m2
|
ISO 180/1U |
|
23°C 8
|
30
|
kJ/m2
|
ISO 180/1U |
|
Instrumented Dart Impact (23°C, Total Energy)
|
45.0
|
J
|
ASTM D3763 |
| Thermal |
額定值
|
單位制
|
測試方法
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
205
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm Span 8
|
205
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
130
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm Span 8
|
130
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
218
|
°C
|
ASTM D1525 9, ISO 306/A50 9 |
|
--
|
150
|
°C
|
ASTM D1525 10, ISO 306/B50 10 |
|
--
|
155
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (123 到 127°C)
|
通過
|
|
IEC 60695-10-2 |
|
CLTE
|
ISO 11359-2 | ||
|
流動 : -40 到 40°C
|
4.1E-5
|
cm/cm/°C
|
|
|
流動 : 23 到 60°C
|
5.0E-5
|
cm/cm/°C
|
|
|
流動 : 23 到 150°C
|
3.6E-5
|
cm/cm/°C
|
|
|
垂直 : -40°C
|
8.1E-5
|
cm/cm/°C
|
|
|
垂直 : 23 到 60°C
|
1.2E-4
|
cm/cm/°C
|
|
|
垂直 : 23 到 150°C
|
2.0E-4
|
cm/cm/°C
|
| Electrical |
額定值
|
|
測試方法
|
|
Dielectric Constant (1 MHz)
|
3.40
|
|
ASTM D150, IEC 60250 |
|
Dissipation Factor (1 MHz)
|
0.020
|
|
ASTM D150, IEC 60250 |
| Fill Analysis |
額定值
|
單位制
|
測試方法
|
|
Melt Viscosity (260°C, 1500 sec^-1)
|
160
|
Pa·s
|
ISO 11443 |
| Additional Information |
額定值
|
單位制
|
測試方法
|
|
填充物
|
10
|
%
|
ASTM D229 |
| Injection |
額定值
|
單位制
|
|
|
Drying Temperature
|
110 到 120
|
°C
|
|
|
Drying Time
|
2.0 到 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Hopper Temperature
|
40 到 60
|
°C
|
|
|
Rear Temperature
|
230 到 245
|
°C
|
|
|
Middle Temperature
|
240 到 255
|
°C
|
|
|
Front Temperature
|
245 到 265
|
°C
|
|
|
Nozzle Temperature
|
240 到 260
|
°C
|
|
|
Processing (Melt) Temp
|
250 到 270
|
°C
|
|
|
Mold Temperature
|
40 到 100
|
°C
|
| 備注 |
| 15.0 mm/min |
| 2類型 1, 5.0 mm/min |
| 31.3 mm/min |
| 42.0 mm/min |
| 5at Yield |
| 6at Break |
| 72 mm/min |
| 880*10*4 mm |
| 9速率 A (50°C/h), 壓 力1 (10N) |
| 10速率 A (50°C/h), 載荷2 (50N) |
點擊下載VALOXVX4910物性表：